• Descriptions

Aerogel Inaulation Blanket  is one of our hot sale products.It has chosen the acupuncture fiber as substrate, and then the aerogel is compounded into the substrate. It has the thermal insulation performance and surface hydrophobicity and excellent flame retardant properties. The thermal conductivity at room temperature in 0.016 (W/m.K), is lower than the static air; The aerogel product is of high hydrophobicity; at room temperature, the water repellent rate of can be up to 99%; Excellent flame retardant performance, and fire rating has met the national A1 standard. And the temperature of the product using range is wide, Joda Aerogel fiberglass blanker could be used according to the different requirements in -200 ~ 650 DEG C for adiabatic pipe and tank, using the furnace of industrial equipment and pipeline.

 

• Technical Parameters

Model		SACB-1-3	SACB-01-6	SACB-1-10
Thickness(mm)		3	6	10
Width(mm)		1400/1500(customizable)
Color		White
Permitted useful temperature range(°C)		-200~650	-200~650	Fiberglass composite: -200~650 Ceramic fiber composite: 600~1000
Density(kg/m³)		200±20	200±20	200±20
Linear expansivity		4.2×10-6
Dimensional stability(max)		1%		Test method GB/T 8811-2008
Compressive property	(min),kpa,@10%	60		Test method GB/T 13480-2014
	(min),kpa,@25%	120		Test method GB/T 13480-2014
Burning behavior		A1		Test method GB/T 20285-2006
The smoke performance level		SR-2
Drip content level		ST-2
Smoke toxicity of the FED's value,(max)		0.1
Corrosion resistance		pass		Test method GB/T 3810.1-2006
Hydrophobicity,(%)		>99.8		Test method GB/T 10299-2011
Tensile strength(min),(kpa)		Fiberglass composite: 100 Ceramic fiber composite: 80		Test method GB/T 17911-2011
Remarks : Silica aerogel fiberglass and ceramic fiber technical parameters

 PS: Aluminum foil's thickness can be Customize

• Advantages

★ Good springiness for fiber

★ Excellent strength and resistance to blowing

★ Chemical stability, erosion resistance

★ Low thermal conductivity

★ Low thermal shrinkage

★ Excellent sound absorption

 

• Application

Filling insulation and joint sealing

Back-up lining for industrial furnaces

Fireproof materials for construction

High temperature materials for filtration

Raw materials for further producing, such as modules